  • 1 University of Mining and Metallurgy Faculty of Material Science and Ceramics al. Mickiewicza 30 30-059 Kraków Poland
  • | 2 Alpol Gips Ltd. Fidor 26-200 Końskie Poland
Restricted access


Calorimetry was applied to an investigation of the early hydration of Portland cement (PC)–calcium aluminate cement (CAC) pastes. The heat evolution measurements were related to the strength tests on small cylindrical samples and standard mortar bars. Different heat-evolution profiles were observed, depending on the calcium aluminate cement/Portland cement ratio. The significant modification of Portland cement heat evolution profile within a few hours after mixing with water was observed generally in pastes containing up to 25% CAC. On the other hand the CAC hydration acceleration effect was also obtained with the 10% and 20% addition of Portland cement. As one could expect the compressive and flexural strength development was more or less changed—reduced in the presence of larger amount of the second component in the mixture, presumably because of the internal cracks generated by expansive calcium sulfoaluminate formation.

Manuscript Submission: HERE

  • Impact Factor (2019): 2.731
  • Scimago Journal Rank (2019): 0.415
  • SJR Hirsch-Index (2019): 87
  • SJR Quartile Score (2019): Q3 Condensed Matter Physics
  • SJR Quartile Score (2019): Q3 Physical and Theoretical Chemistry
  • Impact Factor (2018): 2.471
  • Scimago Journal Rank (2018): 0.634
  • SJR Hirsch-Index (2018): 78
  • SJR Quartile Score (2018): Q2 Condensed Matter Physics
  • SJR Quartile Score (2018): Q2 Physical and Theoretical Chemistry

For subscription options, please visit the website of Springer.

Journal of Thermal Analysis and Calorimetry
Language English
Size A4
Year of
per Year
per Year
Founder Akadémiai Kiadó
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
Publisher Akadémiai Kiadó
Springer Nature Switzerland AG
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
CH-6330 Cham, Switzerland Gewerbestrasse 11.
Chief Executive Officer, Akadémiai Kiadó
ISSN 1388-6150 (Print)
ISSN 1588-2926 (Online)