  • 1 Institute of Construction and Architecture of Slovak Academy of Sciences Dúbravská cesta 9 845 03 Bratislava Slovak Republic
  • | 2 University of New Brunswick Department of Engineering Saint John NB E2L 4L5 Canada
  • | 3 Building Testing and Research Institute Studená 3 Bratislava 821 04 Slovak Republic
Restricted access


Two types of raw materials, original kaolin sand OKS I and OKS II were used for experiment. They were transformed (1 h at 650 °C with 10 °C/min temperature increase) to burnt kaolin sand (BKS I and BKS II) with pozzolanic properties. Contents of decisive mineral—metakaolinite—in BKSs are as follows: BKS I (fraction below 0.06 mm) 20%; BKS II (fraction below 0.06 mm) 36% and BKS II (fraction below 0.1 mm) 31% by mass. Mortars with blends of Portland cement (PC) and BKS were prepared announced as: MK I (0.06) with 5 and 10% cement substitution by metakaolinite; MK II (0.06) with 5 and 10% cement substitution by metakaolinite and MK II (0.1) with 5, 10, 15 and 20% cement substitution by metakaolinite. The reference mortar with 100% of PC was made for comparison. All mortars were adjusted on the constant workability 180 ± 5 mm flow. Besides significant increase in compressive strengths—the refinement of pore structure in mortars with BKS connected with decreases in permeability and Ca(OH)2 content were revealed. The above facts confirm pozzolanic reaction of BKS in contact with hydrated PC and indicate perceptiveness of BKS for the use in cement-based systems as a pozzolanic addition.

Manuscript Submission: HERE

  • Impact Factor (2019): 2.731
  • Scimago Journal Rank (2019): 0.415
  • SJR Hirsch-Index (2019): 87
  • SJR Quartile Score (2019): Q3 Condensed Matter Physics
  • SJR Quartile Score (2019): Q3 Physical and Theoretical Chemistry
  • Impact Factor (2018): 2.471
  • Scimago Journal Rank (2018): 0.634
  • SJR Hirsch-Index (2018): 78
  • SJR Quartile Score (2018): Q2 Condensed Matter Physics
  • SJR Quartile Score (2018): Q2 Physical and Theoretical Chemistry

For subscription options, please visit the website of Springer.

Journal of Thermal Analysis and Calorimetry
Language English
Size A4
Year of
per Year
per Year
Founder Akadémiai Kiadó
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
Publisher Akadémiai Kiadó
Springer Nature Switzerland AG
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
CH-6330 Cham, Switzerland Gewerbestrasse 11.
Chief Executive Officer, Akadémiai Kiadó
ISSN 1388-6150 (Print)
ISSN 1588-2926 (Online)