Following our previous research, this work is dedicated to the study of phase formation in the subsolidus domain of the Bi2O3-PbO-CaO system.
Former investigations performed by DTA/TGA and XRD have pointed out that under non-isothermal conditions only the formation
of binary compounds occurs. Under such conditions these compounds could be non-equilibrium phases.
In order to establish the conditions of formation of equilibrium phases, a study of the Bi2O3-PbO-CaO system, in isothermal conditions, was carried out. The results obtained in isothermal conditions have confirmed the
presence of Bi2O3-rich solid solutions and Ca2PbO4 as main equilibrium phases. An attempt to represent the phase relations of the mentioned system at 700C should be equally