In this work, the influence of attapulgite concentration on the nucleating efficiency of isotactic polypropylene (iPP) and
on the kinetics of non-isothermal crystallization were ascertained.The study was conducted by DSC. The nucleating efficiency
was determined according to the procedure described by Fillon and the kinetics of non-isothermal crystallization was determined
using Ozawa's method using cooling rates of 2, 5 and 10C min−1.Our results indicate that both the relative crystallinity and the crystallization temperature increase with filler content
and that a maximum occurs at 2% mass/mass filler content. Both parameters decrease with increasing cooling rates. The Ozawa's
exponent tended to increase with temperature and filler content.