One of the principal uses of supersulfated cement has been for structures exposed to sea water and sulfate bearing ground waters. The resistance to such environments has been related to the absence of calcium hydroxide and the combination of much of the free alumina into ettringite during hydration. This paper reports the resistance of SSC to sulfate solutions in which ettringite has been decomposed. Prism samples were subjected to initial water storage at 25°C for both 28 days and 6 months. Samples were also cured for 6 months at 95°C and at both 11% and 100% R.H. The control samples of 28 days were compared with the 6 months samples of a more mature undecomposed SSC paste. After curing the prisms were measured and all the samples were immersed in three sulfate solutions (0.7M Na2SO4 , 0.7M MgSO4 and saturated CaSO4), and water at the same time. Measurements of linear expansion over 6 months were carried out. Core and surface material following immersion was examined by DTG and XRD. The study indicated that SSC is resistant to sodium and calcium sulfate solutions. Strong magnesium sulfate solutions decomposed the samples under all conditions. A possible mechanism for this attack is suggested.

Monthly Content Usage

Abstract Views Full Text Views PDF Downloads
Dec 2020 0 0 0
Jan 2021 0 0 0
Feb 2021 1 0 0
Mar 2021 1 0 0
Apr 2021 0 0 0
May 2021 0 0 0
Jun 2021 3 0 0