Condensation of dimethylol-urea (DMU) mixed with urea (U) and collagen hydrolysate (H), obtained through enzymatic hydrolysis of chrome-tanned leather waste, without added acid curing agents in the solid phase was studied through DSC and TG techniques in a temperature interval up to 220°C. Among both techniques TG proved be more useful.While the DMU+U mix produced methylene-oxide (-CH2-O-CH2-) and methylene (-CH2-) bridges at a ratio of approx. 1:1, urea substituted for collagen hydrolysate increased the proportion of more stable methylene bridges to methylene-oxide bridges to a ratio of approx. 2:1. Methylene-oxide bridges are considered to be the main potential sources of formaldehyde emissions from cured urea-formaldehyde type adhesives, and thus the use of collagen hydrolysate in preparation of urea-formaldehyde adhesive types is a suitable way how to make such adhesives more environmental friendly.