Abstract  

With the aim of obtaining materials with applications in pigments, CoxZn7-xSb2O12 spinels were synthesized using the Pechini method. This method consists in the formation of a polymeric net, where the metallic cations are homogeneously distributed. In this work, two types of alcohol (ethyl glycol and ethylene glycol) were used for the synthesis of a zinc antimoniate spinel, CoxZn7-xSb2O12 (x=0-7). The materials were characterized by termogravimetry (TG) and differential thermal analysis (DTA). TG results indicated a decrease in total mass loss when cobalt was added to the solution substituting zinc, for samples prepared using the two different alcohols. Decomposition temperatures, obtained by TG and DTA, presented a decreasing behavior as cobalt was added to the material. In relation to the alcohols, all results indicated a better polymerization of the resin when ethylene glycol was used, being the most indicated one for cation immobilization. X-ray diffraction did not show differences between the two alcohols - both presented the spinel phase (Co, Zn)2.33Sb0.67O4. Samples with higher quantity of cobalt also presented ilmenite phase (Co, Zn)Sb2O6.

Monthly Content Usage

Abstract Views Full Text Views PDF Downloads
Jan 2021 0 0 0
Feb 2021 0 0 0
Mar 2021 0 0 0
Apr 2021 0 0 0
May 2021 0 0 0
Jun 2021 0 0 0
Jul 2021 0 0 0