The purified bentonite parent clay, fraction ≤; 2 mm of montmorillonite type, has been pillared by various polyhydroxy cations, Al, AlFe and AlCu, using conventional pillaring methods. The thermal behavior of PILCs was investigated by combination of X-ray diffraction (XRD), thermal analysis (DTA, TG) and low temperature N2 adsorption/desorption (LTNA). Thermal stability of Al-, AlFe- and AlCu-PILC samples was estimated after isothermal pretreatment in static air on the temperatures 300, 500, 600 and 900C. Crucial structural changes were not registered up to 600C, but the fine changes in interlayer surrounding and porous/microporous structure being obvious at lower temperatures, depending on the nature of the second pillaring ion. AlFe-PILC showed higher thermal stability of the texture, the AlCu-PILC having lower values and lower thermal stability concerning both overall texture and micropore surface and volume. Poorer thermal stability of AlCu-PILC sample at higher temperatures was confirmed, the presence of Cu in the system contributing to complete destruction of aluminum silicate structure, by 'extracting' aluminum in stabile spinel form.

Monthly Content Usage

Abstract Views Full Text Views PDF Downloads
Jan 2021 1 0 0
Feb 2021 0 0 0
Mar 2021 0 0 0
Apr 2021 0 0 0
May 2021 0 0 0
Jun 2021 0 0 0
Jul 2021 0 0 0