The processes of nucleation of Li2O-Al2O3-SiO2 glasses with TiO2 and TiO2+ZrO2 as nucleating agents were discussed. The DTA peak temperature and DTA peak height shown a strong dependence on the nucleation temperature in the glass with TiO2, while in the glass with TiO2+ZrO2 this tendency was small. The optimum nucleation temperatures were 745 and 760°C for two glasses. It suggested that with TiO2+ZrO2 as nucleating agents, the crystallization had lower sensitivity for nucleation temperature, and the glass had higher nucleation efficiency than with TiO2.