  • 1 Bhabha Atomic Research Center Technical Physics and Prototype Engineering Division Mumbai 400 085 India
Restricted access


PbO based phosphate glasses having composition 40P2O5�12Al2O3�6B2O3�9PbO�xNa2O�(33−x)K2O (x=0−33) [F=Na/(Na+K)] have been prepared using conventional melt quench technique. Density, morphology, thermal expansion coefficient (α) and glass transition temperature (Tg) were studied as a function of Na/(Na+K) ratio. Formation of transparent, bubble free and clear glass was observed up to x=18 mol%. Density was found to vary from 2.70 to 3.69 g cm−3. The significant changes were noticed in external morphologies at temperatures corresponding to softening, half ball and melting points under high temperature microscope for three compositions (x=0, 10 and 15 mol%). These glasses recorded the softening and half ball temperatures in the range 454–470�C and 523–576�C respectively and melting temperatures agree well with DTA studies within the experimental limits. Glass transition temperature showed a broad maxima while thermal expansion coefficient (TEC) a broad minima around Na/(Na+K)=0.54. This behaviour is explained on the basis of bond formation/phase separation.

Manuscript Submission: HERE

  • Impact Factor (2019): 2.731
  • Scimago Journal Rank (2019): 0.415
  • SJR Hirsch-Index (2019): 87
  • SJR Quartile Score (2019): Q3 Condensed Matter Physics
  • SJR Quartile Score (2019): Q3 Physical and Theoretical Chemistry
  • Impact Factor (2018): 2.471
  • Scimago Journal Rank (2018): 0.634
  • SJR Hirsch-Index (2018): 78
  • SJR Quartile Score (2018): Q2 Condensed Matter Physics
  • SJR Quartile Score (2018): Q2 Physical and Theoretical Chemistry

For subscription options, please visit the website of Springer.

Journal of Thermal Analysis and Calorimetry
Language English
Size A4
Year of
per Year
per Year
Founder Akadémiai Kiadó
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
Publisher Akadémiai Kiadó
Springer Nature Switzerland AG
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
CH-6330 Cham, Switzerland Gewerbestrasse 11.
Chief Executive Officer, Akadémiai Kiadó
ISSN 1388-6150 (Print)
ISSN 1588-2926 (Online)