Four paste mixtures with varying replacement level of the cement content by fly ash have been studied. Due to fly ash, the
acceleration period decreased and a third hydration peak was noticed with isothermal calorimetry. The total heat after 7 days
increased with increasing fly ash content. From 1 to 7 days, thermogravimetry showed a higher chemically bound water and Ca(OH)2-content for the pastes with fly ash. Between 7 and 14 days the calcium hydroxide started to be depleted due to the pozzolanic
reaction. A unique relation was found between calcium hydroxide and total heat development.