Abstract  

Hydrogen sorption properties and some corresponding changes in the crystallization of amorphous TM33Zr67 (TM=Fe, Co, Ni) alloys have been investigated. Relatively large amount of hydrogen was found to dissolve into the amorphous alloys during electrochemical hydrogen charging. The microstructural evolution during annealing of H-charged Ni33Zr67 was studied as well. The weaker bonded hydrogen desorbs in a large temperature range (440–625 K) before the crystallization of the amorphous alloys to start. A hydride phase (ZrH2) was found to form during annealing the H-charged amorphous Ni33Zr67 alloy. During heating at constant heating rate the hydride decomposes at about 715 K and formation of Zr2Ni immediately takes place. The final microstructure of the Zr2Ni, crystallized from the H-charged matrix, is noticeably finer compared to the material crystallized from the H-free amorphous alloy, most probably due to the higher temperature of Zr2Ni formation in the H-charged amorphous alloy than in the H-free sample.

  • Collapse
  • Expand

To see the editorial board, please visit the website of Springer Nature.

Manuscript Submission: HERE

For subscription options, please visit the website of Springer Nature.

Journal of Thermal Analysis and Calorimetry
Language English
Size A4
Year of
Foundation
1969
Volumes
per Year
1
Issues
per Year
24
Founder Akadémiai Kiadó
Founder's
Address
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
Publisher Akadémiai Kiadó
Springer Nature Switzerland AG
Publisher's
Address
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
CH-6330 Cham, Switzerland Gewerbestrasse 11.
Responsible
Publisher
Chief Executive Officer, Akadémiai Kiadó
ISSN 1388-6150 (Print)
ISSN 1588-2926 (Online)

Monthly Content Usage

Abstract Views Full Text Views PDF Downloads
Oct 2023 1 1 0
Nov 2023 1 0 0
Dec 2023 14 1 0
Jan 2024 3 0 0
Feb 2024 1 0 0
Mar 2024 6 0 0
Apr 2024 1 0 0