Cobalt nanoparticles were synthesized using continuous-flow (CF) chemistry in a stainless steel microreactor for the first time at high output based on the ethanol hydrazine alkaline system (EHAS) producing a yield as high as 1 g per hour [1, 2]. Continuous-flow (CF) synthetic chemistry provides uninterrupted product formation allowing for advantages including decreased preparation time, improved product quality, and greater efficiency. This successful synthetic framework in continuous-flow of magnetic Co nanoparticles indicates feasibility for scaled-up production. The average particle size by transmission electron microscopy (TEM) of the as-synthesized cobalt was 30±10 nm, average crystallite size by Scherrer analysis (fcc phase) was 15±2 nm, and the estimated magnetic core size was 6±1 nm. Elemental surface analysis (X-ray photoelectron spectroscopy [XPS]) indicates a thin CoO surface layer. As-synthesized cobalt nanoparticles possessed a saturation magnetization (Ms) of 125±1 emu/g and coercivity (Hc) of 120±5 Oe. The actual Ms is expected to be greater since the as-synthesized cobalt mass was not weight-corrected (nonmagnetic mass: reaction by-products, solvent, etc.). Our novel high-output, continuous-flow production (>1 g/hr) of highly magnetic cobalt nanoparticles opens an avenue toward industrial-scale production of several other single element magnetic nanomaterials.