Abstract
Thermal stability of a compound forming in a binary system MoO3–In2O3 was investigated by DTA/TG, XRD and SEM methods in this study. For the first time, the diagram of phase equilibria established in the whole range of concentrations of this system's components has been constructed. The temperature and concentration ranges of the components of MoO3–In2O3 system in which the compound In2(MoO4)3 co-exists in solid state with MoO3 or In2O3 or with the liquid were determined. The composition and melting point of the eutectic mixture consisting of In2(MoO4)3 and MoO3 were found.
Introduction
Binary and ternary metal oxide systems have been subjects of intense interest as their characterisation is essential for design of new materials of different types, like semiconductors, magnetic and optical materials or construction materials of specific thermal, mechanical or chemical properties. The above mentioned systems have also been studied in the aspect of testing the catalytic properties of the oxides, their mixtures and phases made by them [1]. An important source of information on the multicomponent oxide systems are the diagrams of phase equilibria reached in them. Such diagrams provide information on the composition, type and thermal stability of compounds and phases formed in a given system as well as on the temperature and concentration ranges of their coexistence in the solid and liquid state [1].
Physicochemical properties, structure and applications of molybdenum(VI) oxide and indium(III) oxide are well known [2–7]. MoO3, In2O3 and In2(MoO4)3 formed as a result of a reaction between the former two, are components of active and selective catalysts of different processes of oxidation of organic compounds, e.g. methanol to formaldehyde, propene to acrylaldehyde or acrylic acid, or benzene to maleic anhydride [8–10]. These oxides have been used in semiconducting sensors for detection of oxidating gases O3 and NO2 [11]. It has been established that the characteristics of the sensors based on MoO3 and In2O3 significantly depend on the conditions of their synthesis, which affect the structure, phase composition and degree of oxidation of molybdenum and indium [11].
To the best of our knowledge, no diagram of phase equilibria has been published for MoO3–In2O3, and the thermal properties of indium(III) molybdate(VI)—the only compound formed in this system—have been only partly recognised. It is known that at ∼340 °C this compound (In2(MoO4)3) undergoes a polymorphous transition from the variety of regular structure (C–In2(MoO4)3, a = 13.34 ± 0.07 Å) [9] to the variety of orthorhombic structure (R–In2(MoO4)3, a = 9.447 Å, b = 9.597 Å, c = 13.29 Å) [10]. The authors of the study [10] gave the melting point of this compound as 1230 °C, however, with no information on the type of the melting process, i.e. whether it is congruent or incongruent.
As indium(III) molybdate(VI) belongs to the group of compounds showing negative thermal expansion and high electric conductivity [12], it can be used as electrolyte in fuel cells (galvanic cells), gas sensors [12] and laser materials [11]. It is also used as a catalyst in the process of production of olefins from paraffin by dehydrogenation with selective combustion of hydrogen [13].
In view of the available literature data, it seemed important to establish the conditions of formation of indium(III) molybdate(VI), determination of its thermal properties and the phase equilibrium diagram of the system MoO3–In2O3 in the whole concentration range of its components.
Experimental
To study the phase equilibria in the MoO3–In2O3 system, 11 samples of MoO3 and In2O3 oxide mixtures were prepared. Contents of the initial mixture, heating conditions and X-ray phase analysis of the samples in the equilibrium state are given in Table 2. All the samples were prepared by solid–solid reactions according to the procedure described inter alia in [14–18].
The phase compositions of the samples, following the successive stages of their heating, were determined on the basis of XRD results (HZG-4, Jena, Germany, Cu-Kα radiation) and the data included in PDF cards. After the last stage of heating, all the samples were subjected to DTA/TG examination. The DTA/TG measurements were performed on a F. Paulik–L. Paulik–L. Erdey derivatograph (the MOM Company, Budapest). The measurements were made in air atmosphere, within the temperature range of 20–1000 °C and at the heating rate of 10 °C/min. All the measurements were made in corundum crucibles. The mass of the samples examined was kept constant at 500 mg. The accuracy of the temperature readout determined on the basis of repetitive tests was established at ±5 °C. The compound In2(MoO4)3 and other selected samples were additionally examined by the DTA/TG method on an SDT 2960 apparatus, made by TA Instruments Company. The measurements were carried out in air atmosphere, within the temperature range of 20–1350 °C, at the heating rate of 10 °C/min. The test was made in corundum crucibles. The mass of the samples examined were ∼15 mg.
A sample of In2(MoO4)3 and a sample of In2(MoO4)3 heated at 935 °C were examined under a scanning electron microscope (JSM-1600, Joel, Japan).
Results and discussion
The white compound obtained in reaction (1) was then subjected to DTA/TG measurements in air atmosphere. The DTA curve of In2(MoO4)3(s) (Fig. 1) revealed two endothermic effects of which the first (a small one) started at 335 °C, while the second started at 1125 °C. On the basis of the literature data [9, 10], the first effect starting at 335 °C was assigned to the polymorphous transition of the regular indium(III) molybdate(VI) to the orthorhombic crystal form of this compound. The temperature of this transition is consistent with the values reported by other authors [9].
DTA and TG curves of In2(MoO4)3
Citation: Journal of Thermal Analysis and Calorimetry 109, 2; 10.1007/s10973-012-2224-7
The second endothermic effect, starting at 1125 °C and of the hitherto unknown origin, was accompanied by a significant mass loss, indicated by TG results and its beginning already at 935 °C. The TG revealed that the mass loss percentage taking place in the range from 935 to 1300 °C was ∼54%. To enable establishing the origin of the second thermal effect appearing on the DTA curve of In2(MoO4)3, the samples of In2(MoO4)3 of the known mass were subjected to additional 1-h heating in a muffle furnace at selected temperatures ranging from 935 to 1250 °C. After such an additional heating, the samples were rapidly cooled to room temperature, weighed, homogenised by grinding and subjected to XRD phase analysis. The temperature of heating, XRD results and the mass loss measured are presented in Table 1.
The phase composition and mass loss after additional heating of In2(MoO4)3
| Heating conditions | 935 °C (1 h) | 1115 °C (1 h) | 1175 °C (1 h) | 1250 °C (1 h) |
|---|---|---|---|---|
| Phases after heating | In2(MoO4)3, In2O3 | In2O3, In2(MoO4)3 | In2O3 | In2O3 |
| Mass loss (%) | 2.33 | 36.50 | 53.00 | 59.85 |
Figure 2 presents the SEM image of pure In2(MoO4)3 (Fig. 2a) and In2(MoO4)3 taken after its heating at 935 °C (Fig. 2b). On the surfaces of the well-developed crystallites of In2(MoO4)3 of diameters ranging from ∼2 to 11 μm, there are small crystallites of In2O3 appearing as a result of decomposition of In2(MoO4)3 beginning at this temperature.
a SEM image of In2(MoO4)3, b SEM image of In2(MoO4)3 heated at 935 °C for 1 h
Citation: Journal of Thermal Analysis and Calorimetry 109, 2; 10.1007/s10973-012-2224-7
The above results have undoubtedly proven that the compound studied does not melt at 1230 °C as suggested by the authors of [10], but it undergoes a thermal decomposition in the solid phase to In2O3 with sublimation of MoO3. In the air atmosphere, this decomposition begins with a low rate even at 935 °C.
Taking into regard the thermal stability of In2(MoO4)3, it seemed interesting to check in which temperature range this compound remains in solid state in equilibrium with the initial oxides MoO3 and In2O3. In order to establish the phase equilibria reached in the MoO3–In2O3 system in air atmosphere, 11 samples of the oxides were prepared of compositions representing the whole range of concentrations of the system studied (Table 2). The homogenised mixtures of the oxides were formed into tablets and subjected to heating in the conditions specified in Table 2, ensuring that the equilibrium state is reached. The contents of initial mixtures, heating conditions and X-ray phase analysis of samples in equilibrium are presented in Table 2.
Contents of initial mixture, heating conditions and X-ray phase analysis of samples in an equilibrium state
| No. | Contents of initial mixtures (mol%) | Heating conditions | Contents of equilibrium samples (mol%) | |
|---|---|---|---|---|
| MoO3 | In2O3 | |||
| 1 | 97.50 | 2.50 | 97.30 MoO3 + 2.70 In2(MoO4)3 | |
| 2 | 95.00 | 5.00 | Stage I: | 94.12 MoO3 + 5.88 In2(MoO4)3 |
| 3 | 90.00 | 10.00 | 400 °C (1 h) → | 85.71 MoO3 + 14.29 In2(MoO4)3 |
| 4 | 85.00 | 15.00 | 500 °C (12 h) → | 72.73 MoO3 + 27.27 In2(MoO4)3 |
| 5 | 80.00 | 20.00 | 550 °C (12 h) | 50.00 MoO3, + 50.00 In2(MoO4)3 |
| 6 | 75.00 | 25.00 | Stage II: | In2(MoO4)3a |
| 7 | 60.00 | 40.00 | 550 °C (12 h) → | 50.00 In2O3 + 50.00 In2(MoO4)3 |
| 8 | 50.00 | 50.00 | 600 °C (24 h) | 66.66 In2O3 + 33.34 In2(MoO4)3 |
| 9 | 40.00 | 60.00 | Stage III: | 77.78 In2O3 + 22.22 In2(MoO4)3 |
| 10 | 25.00 | 75.00 | 600 °C (24 h) | 88.89 In2O3 + 11.11 In2(MoO4)3 |
| 11 | 10.00 | 90.00 | 96.3 In2O3 + 3.70 In2(MoO4)3 | |
The sample additionally heated at 750 °C (24 h)
The XRD phase analysis of all the samples after the first stage of heating up to 550 °C revealed the presence of In2(MoO4)3 besides the initial oxides. After further stages of heating, the samples reached equilibrium. The samples containing in the initial mixtures more than 75.00% mol MoO3 were diphase at equilibrium and contained MoO3 and In2(MoO4)3. Sample 6 of the initial mixture composition corresponding to the stoichiometry of In2(MoO4)3, after the last stage of heating, contained only In2(MoO4)3. In the samples representing the remaining range of concentrations of the system components, i.e. below 75% mol MoO3, the presence of In2(MoO4)3 in equilibrium with In2O3 was found. The heating of the samples was accompanied by a small change in their mass. Total percentage of mass loss of the samples after all the stages of their heating varied from 0.16 to 1.07%. The greatest mass loss that was noted for the samples contained in the initial mixtures was ranging from 75.00 to 97.50% mol MoO3.
This observation means that the mass loss is attributed mostly to MoO3 which, to a small degree, underwent sublimation during heating. In consistence with the literature data, the sublimation of MoO3 begins even at 550 °C [19, 20].
Although the sublimation of MoO3 from the reaction mixtures of the oxides studied leads to a small change in their composition, the mixtures still represent the system MoO3–In2O3. The small magnitude of the mass losses makes them irrelevant for the purpose of the study. All the samples in equilibrium were further subjected to the DTA/TG measurements.
The DTA curves recorded for the samples, which at equilibrium were mixtures of MoO3 with In2(MoO4)3 (Table 2, samples 1–5) in the range from ∼20 to 1000 °C, showed one well-developed endothermic effect beginning at ∼780 °C. The DTA curves of the other samples at the state of equilibrium, i.e. the samples containing In2(MoO4)3 and In2O3 (Table 2, samples 6–11) did not show any large thermal effects in this temperature range. Only on the DTA curves recorded for samples 4–7 and 8, containing at equilibrium the greatest amounts of In2(MoO4)3 in a mixture with MoO3 or In2O3, a very small thermal effect was observed at ∼335 °C, corresponding to a polymorphic transition of indium(III) molybdate(VI) [9].
The shape of the thermal effect starting at 780 ± 5 °C and the fact that it decreased with increasing content of In2(MoO4)3 in the samples indicated that the effect corresponds to the melting of eutectic mixture forming of In2(MoO4)3 and MoO3. Moreover, this effect was the greatest and most symmetric on the DTA curve of sample 1 (Table 2), which allowed concluding that the content of In2(MoO4)3 in the eutectic mixture with MoO3 was 2.70% mol or lower.
In order to establish the composition of eutectic mixture, four additional samples were prepared containing 2.5; 2.0; 1.5 and 1.0% mol In2(MoO4)3 in mixtures with MoO3 and studied by DTA. The most pronounced and most symmetric effect starting at 780 ± 5 °C was noted on the DTA curve of the sample with 2.5% mol In2(MoO4)3. On the DTA curves of the other three samples, this thermal effect was much smaller and had a poorly developed maximum (not a clearly pointed peak). For the sample containing 1.0% mol In2(MoO4)3 this effect was recorded with a clearly marked inflection from the side of lower temperatures.
The above results imply that In2(MoO4)3 and MoO3 make the eutectic mixture composed of 2.5% mol In2(MoO4)3 and 97.50% mol MoO3, which when expressed in the content of MoO3–In2O3 corresponds to ∼2.3% mol In2O3 and melts at 780 ± 5 °C.
Figure 3 presents the DTA curve of the sample composition of which corresponds to that of the eutectic mixture (Fig. 3a) and that of the sample containing 1.0% mol of In2(MoO4)3 (Fig. 3b) containing an excess of MoO3 relative to the composition of the eutectic mixture.
DTA curve of a eutectic mixture composed of 2.5% mol In2(MoO4)3 and 97.50% mol MoO3, b the sample containing an excess of MoO3 relative to the composition of the eutectic mixture
Citation: Journal of Thermal Analysis and Calorimetry 109, 2; 10.1007/s10973-012-2224-7
The samples containing In2(MoO4)3 and In2O3 at the equilibrium state (Table 2, samples 7–11) were further subjected to DTA/TG study in the range from ∼20 to 1350 °C. The effects on the DTA/TG curves started at the same temperatures as the effects recorded on the DTA/TG curves recorded for pure In2(MoO4)3 (Fig. 1); however, the difference was in the size, and for the former samples, their sizes distinctly decreased with decreasing content of In2(MoO4)3. This observation allowed us to conclude that In2(MoO4)3 remains at equilibrium with In2O3 in solid state up to the temperature of In2(MoO4)3 decomposition, i.e. 935 °C.
The DTA/TG and XRD (phase analysis) results obtained for the samples at equilibrium were the basis for construction of the phase diagram of MoO3–In2O3 in the entire range of concentrations of the components, up to 935 °C (Fig. 4). This diagram was constructed according to the procedure described, among other things in the studies [21–26].
Phase diagram of the MoO3–In2O3 system. filled circle points indicated DTA, open circle points indicated TG, times XRD analysis after quenched
Citation: Journal of Thermal Analysis and Calorimetry 109, 2; 10.1007/s10973-012-2224-7
The types of solid phases being at equilibrium with the liquid were identified on the basis of additional studies. In these additional studies, selected samples at equilibrium were heated for 1 or 3 h at temperatures chosen from that corresponding to the solidus line to 1000 °C. After this additional heating, the samples were rapidly quenched to room temperature, and after homogenisation by grinding, they were subjected to phase analysis by XRD. The compositions of these samples and the temperatures at which they were additionally heated are given in the diagram. The areas of the sample existence at equilibrium determined on the basis DTA and XRD methods are delineated by solid lines, while those established only on the basis of the XRD data for the additionally heated samples are marked with broken lines.
Conclusions
Analysis of the results obtained in the study permitted drawing the following conclusions:
In2(MoO4)3 is the only compound forming in the binary system of MoO3–In2O3 oxides, and it is stable in the air atmosphere up to ∼935 °C. Above this temperature, the compound starts thermal decomposition to In2O3 and MoO3 accompanied by sublimation of the latter oxide.
Indium(III) molybdate(VI) in solid state remains in equilibrium with MoO3 up to 780 °C, i.e. to the melting point of the eutectic mixture formed between these compounds.
The eutectic mixture of the composition of 2.5% mol In2(MoO4)3 and 97.5% mol MoO3 when expressed in the contents of the mixture components, corresponds to the content of In2O3 of 2.3% mol.
Indium(III) molybdate(VI) co-exists in solid state with In2O3 up to ∼935 °C.
The system MoO3–In2O3 in the range of components not exceeding 25% mol In2O3, is a real binary system also above the solidus line.
References
1. Changkang, C 1998 Phase diagram and its application to the crystal growth of high TC oxide superconductors. Prog Cryst Growth Charact 36:1–97 .
2. Wyckoff, RWG 1965 Crystal structures Interscience/Wiley New York.
3. He, T, Yao, J 2003 Photochromism of molybdenum oxide. J Photochem Photobiol C Photochem Rev 4:125–143 .
4. Gurlo, A, Bârsan, N, Ivanovskaya, M, Weimar, U, Göpel, W 1998 In2O3 and MoO3–In2O3 thin film semiconductor sensors: interaction with NO2 and O3. Sens Actuators B 47:92–99 .
5. Epifani, M, Siciliano, P, Gurlo, A, Barsan, N, Weimar, U 2004 Ambient pressure synthesis of corundum—type In2O3. J Am Chem Soc 126:4078–4079 .
6. Solov'eva, AE 1987 Phase transformations in polycrystalline indium oxide. Refract Ind Ceram 28:380–385.
7. Yu, D, Wang, D, Qian, Y 2004 Synthesis of metastable hexagonal In2O3 nanocrystals by a precursor—dehydratation route under ambient pressure. J Solid State Chem 177:1230–1234 .
8. Klevtsov, PW 1968 Sintez kristallov molibdata india In2(MoO4)3. Neorg Mater 4:345–372.
9. Trunov, VK, Kovba, LM 1967 O wzaimodeistvii In2O3 s WO3 i MoO3. Vestn Mosk Univ 1:114–116.
10. Steiner, U, Reichelt, W 2005 Chemischer Transport ternärer Indiummolybdate. Z Anorg Allg Chem Dresden 631:1877–1884 .
11. Nassau, K, Levinstein, HJ, Loiacono, GM 1965 A comprehensive study of trivalent tungstates and molybdates of the type L2(MO4)3. J Phys Chem Solids 26:1805–1816 .
12. Maczka, M, Hermanowicz, K, Hanuza, J 2005 Phase transition and vibrational properties of A2(BO4)3 compounds (A = Sc, In; B = Mo, W). J Mol Struct 283–288:744–747.
13. Marinkovic, BA, Ari, M, Jardim, PM, Avilezde, RR, Rizoo, F, Ferreeira, FF 2010 In2Mo3O12: a low negative thermal expansion compound. Thermochim Acta 499:48–53 .
14. Blonska-Tabero, A, Bosacka, M, Dabrowska, G, Filipek, E, Piz, M, Rychlowska-Himmel, I, Tabero, P, Tomaszewicz, E 2008 The synthesis and properties of the phases obtained by solid–solid reactions. J Mining Metall 44B:19–26 .
15. Bosacka, M, Blonska-Tabero, A 2008 Reinvestigation of system CdO–V2O5 in the solid state. J Therm Anal Calorim 93:811–815 .
16. Filipek, E, Dąbrowska, G, Piz, M 2010 Synthesis andcharacterization of new compound in the V–Fe–Sb–O system. J Alloy Compd 490:93–97 .
17. Filipek, E, Piz, M 2010 The reactivity SbVO5 with T-Nb2O5 in the solid state in air. J Therm Anal Calorim 101:447–453 .
18. Sulcova, P, Vitaskova, L, Trojan, M 2010 Thermal analysis of the Ce1−xTbxO2 pigments. J Therm Anal Calorim 99:409–413 .
19. Samant, MS, Kerkar, AS, Bharadwaj, SR, Dharwadkar, SR 1992 Thermodynamic investigation of the vaporization of molybdenym trioxide. J Alloys Compd 187:373–379 .
20. Postnikov, AYu, Gavrilov, PI Tarasova 1999 Mechanism of interaction of BaO and MoO3 in a combustion wave. Combust Explos Whock Waves 35:514–517 .
21. Walczak, J, Filipek, E 1990 Studies on the V2O5–CrVMoO7 system. Thermochim Acta 173:235–240 .
22. Walczak, J, Kurzawa, M, Filipek, E 1987 Phase equilibria in the system Fe2(MoO4)3–V2O5. Thermochim Acta 117:9–15 .
23. Filipek, E 1999 Phase equilibria in the V2O5–Sb2O4 system. J Therm Anal Calorim 56:159–165 .
24. Filipek, E, Dabrowska, G 2007 Synthesis and selected properties of CrSbVO6 and phase relations in the V2O5–Cr2O3–Sb2O4 system. J Mater Sci 42:4905–4915 .
25. Filipek, E, Dabrowska, G 2009 Phase relations up to the solidus line in the part of the Sb–Zn–O system. Central Eur J Chem 7:192–196 .
26. Radominska, R, Znamierowska, T, Szuszkiewicz, W 2011 Phase equilibria in the system Rb3PO4-Ba3(PO4)2. J Therm Anal Calorim 103:761–766 .