Commercial light-cured dental composites were used in this study. Two laboratorial composites, Resilab (Wilcos/Brazil), Epricord (Kuraray/Japan) were compared under cured and uncured conditions. Thermal analysis, infrared spectroscopy and scanning electron microscopy were used to evaluate the dental composites. The mass change and heat flow signals (TG–DSC) were recorded simultaneously by using STA 409 PC Luxx (NETZSCH), in the 25–800 °C temperature range at a heating rate of 10 °C/min under nitrogen atmosphere (70 mL/min). Employing thermo-microbalance TG 209 C F1 Iris (NETZSCH) coupled to the BRUKER Optics FTIR TENSOR, the samples were analyzed by combined thermogravimetric and spectroscopic methods (TG–FTIR). The initial sample mass was about ~12 mg, the data collection have been done in the 35–800 °C temperature range at a heating rate of 20 K/min in nitrogen atmosphere (flow rate: 40 mL/min). Finally, superficial topographic was analyzed by scanning electron microscopy (SEM). Dental composite evaluation suggests a high thermal stability and inorganic content in RES D sample. Degrees of conversion (DC) values were almost the same and there was no direct relationship between DC and amount of particles and size. Similar compositions were found in all samples.

Manuscript Submission: HERE

  • Impact Factor (2019): 2.731
  • Scimago Journal Rank (2019): 0.415
  • SJR Hirsch-Index (2019): 87
  • SJR Quartile Score (2019): Q3 Condensed Matter Physics
  • SJR Quartile Score (2019): Q3 Physical and Theoretical Chemistry
  • Impact Factor (2018): 2.471
  • Scimago Journal Rank (2018): 0.634
  • SJR Hirsch-Index (2018): 78
  • SJR Quartile Score (2018): Q2 Condensed Matter Physics
  • SJR Quartile Score (2018): Q2 Physical and Theoretical Chemistry

For subscription options, please visit the website of Springer.

Journal of Thermal Analysis and Calorimetry
Language English
Size A4
Year of
per Year
per Year
Founder Akadémiai Kiadó
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
Publisher Akadémiai Kiadó
Springer Nature Switzerland AG
H-1117 Budapest, Hungary 1516 Budapest, PO Box 245.
CH-6330 Cham, Switzerland Gewerbestrasse 11.
Chief Executive Officer, Akadémiai Kiadó
ISSN 1388-6150 (Print)
ISSN 1588-2926 (Online)